Boiler Tube
JIS G3456 Carbon Steel Pipes
Carbon Steel Pipes for High Temperature Service
JIS G3456 STPT 370 Carbon Steel Pipes mainly used for piping at a temperature over 350℃.
Manufacture:Seamless or electric resistance welding process
Out Dimensions: 14mm-508mm
Wall Thickness: 2mm-60mm
Length: Fixed(6m,9m,12,24m) or normal length(5-12m)
Ends: Plain End, Beveled End, Threaded
Method of Manufacture
(1)JIS G3456 STPT 370 Carbon Steel Pipes are manufactured from coarse-grained killed steel by the seamless or electric resistance welding process
(2)When required by the purchaser, the pipe may be furnished with the bevel end.
Heat treatment
| Grade | Hot finished seamless steel pipe | Cold finished seamless steel pipe | Hot finished electric resistance welded steel pipe | Electric resistance welded steel pipe other than hot finished |
| STPT370 | As manufactured. However, low temperature annealing or normalizing may be applied, as necessary. | Low temperature annealed or normalized. | As manufactured. However, low temperature annealing or normalizing may be applied, as necessary. | Low temperature annealed or normalized. |
Chemical Composition of JIS G3456 STPT 370
| Grade | Chemical Composition % | ||||
| C | Si | Mn | p | S | |
| STPT 370 | 0.25 max. | 0.10~0.35 | 0.30~0.90 | 0.035 max. | 0.035 max. |
Mechanical Properties of JIS G3456 STPT 370
| Letter symbol of grade | Mechanical Properties | |||||
| Tensile strength | Yield strength | Elongation % | ||||
| kgf/m㎡ {N/ m㎡} | kgf/m㎡ {N/ m㎡} | No.11 and No.12 test pieces | No. 5 test pieces | No. 4 test piece | ||
| Longitudinal | Transverse | Longitudinal | Transverse | |||
| STPT370 | 38 {373}min | 22{216} min | 30 min | 25 min | 23 min | 28 min |
Appearance
(1)The pipe are practically straight, and its both ends shall be at a right angle to its axis.
(2) The inside and outside surfaces of the pipe shall be well-finished and free form defects that are detrimental to practical use.
Dimensions Tolerance of JIS G3456
| Division | Tolerances on outside diameter | Tolerances on wall thickness | Tolerance on deviation in wall thickness |
| Hot finished seamless steel pipe | Up to 50 mm 【0.5mm | ≤Up to 4 mm 【0.5mm | Up to and incl. 20 % of wall thickness |
| 50mm and over, up to 160mm 【1% | |||
| 160mm and over, up to 200mm 【1.6mm | ≤4mm and over 【12.5% | ||
| 200mm and over 【0.8% | |||
| However, for pipes 350mm and over in diameter, the length of circumference may substitute as a basis for tolerances, In this case, the tolerances shall be 【0.5%. | |||
| Cold finished seamless steel pipe and electric resistance welded steel pipe | Up to 40mm 【0.3mm | ≤Up to 2 mm 【0.2mm | – |
| 40mm and over 【0.8% | ≤2mm and over 【10% | ||
| However, for pipes 350mm and over in diameter, the length of circumference may substitute as a basis for tolerances. In this case, the tolerances shall be 【0.5% |
Testings
(1)Chemical analysis
(2)Tensile Test
(3)Flattening Test
(4) Bending Test
(5) Hydrostatic Test or Nondestructive Examination
Report
We will submit to the purchaser the report on the test results, method of manufacture, ordered dimensions, quantity and work lot number traceable to the manufacturing conditions, etc.
JIS G3456 STPT 410 Carbon Steel Pipes mainly used for piping at a temperature over 350℃.
Manufacture:Seamless or electric resistance welding process
Out Dimensions: 14mm-508mm
Wall Thickness: 2mm-60mm
Length: Fixed(6m,9m,12,24m) or normal length(5-12m)
Ends: Plain End, Beveled End, Threaded
Method of Manufacture
(1)JIS G3456 STPT 410 Carbon Steel Pipes are manufactured from coarse-grained killed steel by the seamless or electric resistance welding process
(2)When required by the purchaser, the pipe may be furnished with the bevel end.
Heat treatment
| Grade | Hot finished seamless steel pipe | Cold finished seamless steel pipe | Hot finished electric resistance welded steel pipe | Electric resistance welded steel pipe other than hot finished |
| STPT410 | As manufactured. However, low temperature annealing or normalizing may be applied, as necessary. | Low temperature annealed or normalized. | As manufactured. However, low temperature annealing or normalizing may be applied, as necessary. | Low temperature annealed or normalized. |
| Grade | Chemical Composition % | ||||
| C | Si | Mn | p | S | |
| STPT 410 | 0.30 max. | 0.10~0.35 | 0.30~1.00 | 0.035 max. | 0.035 max. |
Mechanical Properties of JIS G3456 STPT 410
| Letter symbol of grade | Mechanical Properties | |||||
| Tensile strength | Yield strength | Elongation % | ||||
| kgf/m㎡ {N/ m㎡} | kgf/m㎡ {N/ m㎡} | No.11 and No.12 test pieces | No. 5 test pieces | No. 4 test piece | ||
| Longitudinal | Transverse | Longitudinal | Transverse | |||
| STPT 410 | 42{412}min | 25{245} min | 25 min | 20 min | 19 min | 24 min |
Appearance
(1)The pipe are practically straight, and its both ends shall be at a right angle to its axis.
(2) The inside and outside surfaces of the pipe shall be well-finished and free form defects that are detrimental to practical use.
Dimensions Tolerance of JIS G3456
| Division | Tolerances on outside diameter | Tolerances on wall thickness | Tolerance on deviation in wall thickness |
| Hot finished seamless steel pipe | Up to 50 mm 【0.5mm | ≤Up to 4 mm 【0.5mm | Up to and incl. 20 % of wall thickness |
| 50mm and over, up to 160mm 【1% | |||
| 160mm and over, up to 200mm 【1.6mm | ≤4mm and over 【12.5% | ||
| 200mm and over 【0.8% | |||
| However, for pipes 350mm and over in diameter, the length of circumference may substitute as a basis for tolerances, In this case, the tolerances shall be 【0.5%. | |||
| Cold finished seamless steel pipe and electric resistance welded steel pipe | Up to 40mm 【0.3mm | ≤Up to 2 mm 【0.2mm | – |
| 40mm and over 【0.8% | ≤2mm and over 【10% | ||
| However, for pipes 350mm and over in diameter, the length of circumference may substitute as a basis for tolerances. In this case, the tolerances shall be 【0.5% |
Testings
(1)Chemical analysis
(2)Tensile Test
(3)Flattening Test
(4) Bending Test
(5) Hydrostatic Test or Nondestructive Examination
Report
We will submit to the purchaser the report on the test results, method of manufacture, ordered dimensions, quantity and work lot number traceable to the manufacturing conditions, etc.
JIS G3456 STPT 480 Carbon Steel Pipes mainly used for piping at a temperature over 350℃.
Manufacture:Seamless process
Out Dimensions: 14mm-508mm
Wall Thickness: 2mm-60mm
Length: Fixed(6m,9m,12,24m) or normal length(5-12m)
Ends: Plain End, Beveled End, Threaded
Method of Manufacture
(1)JIS G3456 STPT 480 Carbon Steel Pipes are manufactured by the seamless process.
(2)When required by the purchaser, the pipe may be furnished with the bevel end.
Heat treatment
| Grade | Hot finished seamless steel pipe | Cold finished seamless steel pipe |
| STPT480 | As manufactured. However, low temperature annealing or normalizing may be applied, as necessary. | Low temperature annealed or normalized. |
Chemical Composition of JIS G3456 STPT 480
| Grade | Chemical Composition % | ||||
| C | Si | Mn | p | S | |
| STPT 480 | 0.33 max. | 0.10~0.35 | 0.30~1.00 | 0.035 max. | 0.035 max. |
Mechanical Properties of JIS G3456 STPT 480
| Letter symbol of grade | Mechanical Properties | |||||
| Tensile strength | Yield strength | Elongation % | ||||
| kgf/m㎡ {N/ m㎡} | kgf/m㎡ {N/ m㎡} | No.11 and No.12 test pieces | No. 5 test pieces | No. 4 test piece | ||
| Longitudinal | Transverse | Longitudinal | Transverse | |||
| STPT 480 | 49{481} min. | 28{275} min. | 25 min. | 20 min. | 17 min. | 22 min. |
Appearance
(1)The pipe are practically straight, and its both ends shall be at a right angle to its axis.
(2) The inside and outside surfaces of the pipe shall be well-finished and free form defects that are detrimental to practical use.
Dimensions Tolerance of JIS G3456
| Division | Tolerances on outside diameter | Tolerances on wall thickness | Tolerance on deviation in wall thickness |
| Hot finished seamless steel pipe | Up to 50 mm 【0.5mm | ≤Up to 4 mm 【0.5mm | Up to and incl. 20 % of wall thickness |
| 50mm and over, up to 160mm 【1% | |||
| 160mm and over, up to 200mm 【1.6mm | ≤4mm and over 【12.5% | ||
| 200mm and over 【0.8% | |||
| However, for pipes 350mm and over in diameter, the length of circumference may substitute as a basis for tolerances, In this case, the tolerances shall be 【0.5%. | |||
| Cold finished seamless steel pipe | Up to 40mm 【0.3mm | ≤Up to 2 mm 【0.2mm | – |
| 40mm and over 【0.8% | ≤2mm and over 【10% | ||
| However, for pipes 350mm and over in diameter, the length of circumference may substitute as a basis for tolerances. In this case, the tolerances shall be 【0.5% |
Testings
(1)Chemical analysis
(2)Tensile Test
(3)Flattening Test
(4) Bending Test
(5) Hydrostatic Test or Nondestructive Examination
Report
We will submit to the purchaser the report on the test results, method of manufacture, ordered dimensions, quantity and work lot number traceable to the manufacturing conditions, etc.